Universal Scaling Behaviors of Entangled Polymer Melts at High-stress Shear
Abstract
In addition to the terminal flow (the region I) and the shear thinning (the region II), we discover two new flow regions in capillary flow at the wall stress higher than the plateau modulus of the polymer. The region III violates the empirical Cox-Merz rule with a significantly weaker shear thinning than the region II, and the region IV exhibits unexpected shear thickening. Moreover, the crossover shear rates between the regions II and III and between the regions III and IV scale with the number of entanglement per chain, Z=M_w/M_e, as Z^(-2.0) and Z^(-1.2) respectively. We attribute the weakening in shear thinning and the emergence of shear thickening to the deformation-induced non-Gaussian stretching of polymers. These observations offer the first experimental quantification of the deformation behaviors of polymer melts at high-stress shear.
- Publication:
-
arXiv e-prints
- Pub Date:
- May 2020
- DOI:
- 10.48550/arXiv.2005.01251
- arXiv:
- arXiv:2005.01251
- Bibcode:
- 2020arXiv200501251X
- Keywords:
-
- Condensed Matter - Soft Condensed Matter;
- Condensed Matter - Materials Science
- E-Print:
- While the first three regions are confirmed, the data of region IV in this article was confirmed to be from a different origin other than polymer chain dynamics that makes the data of region IV not appropriate to compare directly with other three regions