Surface nickel particles generated by exsolution from a perovskite structure
Abstract
LaAl1-xNixO3 (with x = 0.05 and 0.2) perovskite oxides were successfully synthesized and its behavior under reduction atmosphere was studied. HRTEM and STEM studies, coupled to HAADF and EDX detection, allowed to evidence the Ni exsolution process to the surface of the solid and to build nano-catalytic centers. The size of these centers is independent of the reduction conditions in the range studied. The high specific surface of the raw material, its porosity and the structure defects could be responsible of the low temperature at which the exsolution process starts. The content of Ni dopants allows the control of Ni centers size on the surface and the synthesis method provides Ni-nanoparticles strongly anchored to the resultant support.
- Publication:
-
Journal of Solid State Chemistry France
- Pub Date:
- May 2019
- DOI:
- 10.1016/j.jssc.2019.02.036
- Bibcode:
- 2019JSSCh.273...75A
- Keywords:
-
- Ni particles;
- Perovskites;
- Exsolution process;
- Reduction conditions;
- TEM