MOVPE deposition and optical properties of thin films of a Bi2Te3-x Se x topological insulator
Abstract
A set of monocrystalline B2Te3-x Se x films of various compositions were synthesized by metalorganic vapor epitaxy. The smooth films with thicknesses of about 500 nm were grown on (0001) Al2O3 substrates at 465 °C using trimethylbismuth, diethyltellurium and diisopropylselenium as meta-organic precursors. The epitaxial nature of the films and their rhombohedral crystal structure are confirmed by X-ray studies and Raman spectroscopy. The elemental composition of the films was determined by energy dispersive X-ray spectrometry. Optical properties of Bi2Te3-x Se x films were examined in the 260-1000 nm range by multi-angle spectroscopic ellipsometry (SE). It was shown that the optical properties of Bi2Te3-x Se x films vary monotonically depending on the ratio of selenium to tellurium. It is demonstrated that SE can be used for rapid assessment of the composition of Bi2Te3-x Se x films.
- Publication:
-
Journal of Physics Conference Series
- Pub Date:
- March 2019
- DOI:
- 10.1088/1742-6596/1199/1/012038
- Bibcode:
- 2019JPhCS1199a2038K