High pressure synthesis, crystal growth and magnetic properties of TiOF
Abstract
Polycrystalline samples of TiOF have been prepared at 1300 °C and 8 GPa, with small single crystals grown at the same conditions. The crystal structure remains tetragonal rutile-type down to at least 90 K (space group P42/mnm, a = 4.6533 (2) Å and c = 3.0143 (2) Å at 90 K) and the Ti(O,F)6 octahedra are slightly compressed, consistent with Jahn-Teller distortion of 3d1 Ti3+. Diffuse scattering reveals disordered structural correlations that may arise from local cis-order of oxide anions driven by covalency. TiOF is paramagnetic down to 5 K and observation of a small paramagnetic moment and a substantial Pauli term indicates that the d-electrons are partially delocalised.
- Publication:
-
Solid State Sciences
- Pub Date:
- June 2018
- DOI:
- 10.1016/j.solidstatesciences.2018.03.018
- Bibcode:
- 2018SSSci..80...35C