Characterization of cement composites based on recycled cellulosic waste paper fibres

Nowadays, there is paying an attention to the utilization of natural, renewable and biodegradable resources of raw materials of lignocellulosic character, residues from agricultural crops and wood processing as well as waste from papermaking industry in building composite materials preparing. Also recycled fibres coming from waste paper are considered as valuable material. The objective of this study is to utilize these recycled cellulosic fibres into cement composites and characterise their impact on resulting physical and mechanical properties of fresh and hardened cement composites. Manufactured cement composites contained 0.2%, 0.3% and 0.5% addition of cellulosic fibres. In fresh fibre cement mixtures reduction in workability with increasing amount of cellulose fibres was noticed. Density as well as compressive and flexural strength of 28 and 90 days hardened fibre cement composites was tested. Distribution of cellulosic fibres with 0.5% addition in hardened fibre cement composites was also observed. The results of density determination of 28 and 90 days hardened fibre cement composites showed reduction in their values related to weight lighter concretes. Compressive strengths of fibre cement composites have shown decreasing character with increasing added amount of cellulosic fibres into the mixture up to 0.5%. Maximal decrease in compressive strength values was observed in composites containing 0.5% of cellulosic fibres. However, obtained strength parameter values of hardened composites had satisfying results for their application in construction as non-load bearing building material.