Excitation-dependent carrier lifetime and diffusion length in bulk CdTe determined by time-resolved optical pump-probe techniques
Abstract
We applied time-resolved pump-probe spectroscopy based on free carrier absorption and light diffraction on a transient grating for direct measurements of the carrier lifetime and diffusion coefficient D in high-resistivity single crystal CdTe (codoped with In and Er). The bulk carrier lifetime τ decreased from 670 ± 50 ns to 60 ± 10 ns with increase of excess carrier density N from 1016 to 5 × 1018 cm-3 due to the excitation-dependent radiative recombination rate. In this N range, the carrier diffusion length dropped from 14 μm to 6 μm due to lifetime decrease. Modeling of in-depth (axial) and in-plane (lateral) carrier diffusion provided the value of surface recombination velocity S = 6 × 105 cm/s for the untreated surface. At even higher excitations, in the 1019-3 × 1020 cm-3 density range, D increase from 5 to 20 cm2/s due to carrier degeneracy was observed.
- Publication:
-
Journal of Applied Physics
- Pub Date:
- January 2018
- DOI:
- 10.1063/1.5010780
- Bibcode:
- 2018JAP...123b5704S