Interfacial morphology evolution of KTa1-xNbxO3 crystal growth
Abstract
Two-dimensional growth of Potassium tantalate niobate (KTa1-xNbxO3) crystals with x = 0.94 was visualized by a high-temperature in situ observation system. Moreover, the interfacial morphology evolution and the interfacial kinetics during crystal growth were systematically studied by optical microscope. It was found that a square-shaped crystal surrounded by {1 1 0} planes was formed in the melt with small undercooling degree, while a large amount of rod-shaped crystals along with [0 0 1] direction predominated under large undercooling conditions. XRD results proved the orthorhombic phase of both shaped crystals. Interfacial kinetics analysis demonstrated the two-dimensional nucleation mechanism in the growth of square-shaped crystal. In contrast, the rod-shaped crystals were inclined to the rough surface growth mechanism. Furthermore, the surface compositional distribution of the as-grown crystal was carried out by EMPA, indicating that rod-shaped crystals had a smaller composition fluctuation than the square-shaped one, mainly due to the depressed segregating effect by the faster growth rate. The analysis of the mechanism and performance can promote the understanding of the KTN crystal.
- Publication:
-
Journal of Crystal Growth
- Pub Date:
- June 2017
- DOI:
- 10.1016/j.jcrysgro.2017.03.032
- Bibcode:
- 2017JCrGr.467...77L
- Keywords:
-
- A1. Crystal growth;
- A1. Interfacial morphology;
- A1. Kinetics;
- A2. In situ observation;
- B1. Potassium tantalate niobate