Temperature dependent structural and magnetic study of Co-sputtered Fe-Al thin film
Abstract
The authors have deposited co-sputtered Fe-Al thin film on a glass substrate. It is the first ever reporting of Fe and Al co-sputtering in an Argon atmosphere under vacuum conditions. The sample was annealed at 200°C, 300°C, 400°C, so as to allow different phase formation in it. To study the structural and magnetic properties of the samples the GIXRD, XRR and MOKE measurements were done. After annealing at 400°C we observed disordered FeAl formation and which after further converted to more ordered phase which is also confirmed from reflectivity measurements. The magnetic measurement shows the magnetic nature of the sample even after annealing at 400°C/5hr.