Growth Kinetics of γ-Al12Mg17 and β-Al3Mg2 Intermetallic Phases in Mg vs. Al Diffusion Couples
Abstract
Increasing use and development of lightweight Mg-alloys have led to the desire for more fundamental research in and understanding of Mg-based systems. As a strengthening component, Al is one of the most important and common alloying elements for Mg-alloys. In this study, solid-to-solid diffusion couple techniques were employed to examine the interdiffusion between pure Mg and Al. Diffusion anneals were carried out at 300°, 350°, and 400°C for 720, 360, and 240 hours, respectively. Optical and scanning electron microscopies (SEM) were employed to observe the formation of the intermetallics γ-Al12Mg17 and β-Al3Mg2, but not ɛ-phase. Concentration profiles were determined using X-ray energy dispersive spectroscopy (XEDS). The growth constants and activation energies were determined for each intermetallic phase.
- Publication:
-
Magnesium Technology 2011
- Pub Date:
- 2016
- DOI:
- 10.1007/978-3-319-48223-1_101
- Bibcode:
- 2016mt11.book..549B
- Keywords:
-
- Materials Science