A comparison of rapid-annealed FePt and FePd thin films: Internal stress, L10 ordering, and texture
Abstract
Effect of rapid thermal annealing (RTA) on the crystallographic orientation and magnetic properties in single-layered FePt and FePd films has been characterized. A huge biaxial tensile stress of ∼2 GPa was induced in the L10-FePt thin films after an RTA of 800 °C, which resulted in a significant orientation transition from (111) to (001) texture. On the other hand, in case of the FePd films, only a small in-plane tensile stress (∼0.5 GPa) was accumulated, which caused that the orientation barely changed from a (111) texture to isotropic state. These results suggest that the high ordering temperature and low tensile stress were the likely reasons why RTA has no effect on texture formation of the FePd films.
- Publication:
-
Vacuum
- Pub Date:
- March 2016
- DOI:
- 10.1016/j.vacuum.2015.11.022
- Bibcode:
- 2016Vacuu.125....1H
- Keywords:
-
- FePt thin films;
- FePd thin films;
- Rapid thermal annealing;
- Preferred orientation