The Origin of Hierarchical Structure in Self-Assembled Graphene Oxide Papers and the Effect on Mechanical Properties
Abstract
The quest for new materials with ever improving properties has motivated interest in bulk nanostructured materials. Graphene, a two-dimensional sheet of hexagonally arranged carbon atoms, has been of particular interest given its exceptional mechanical, thermal, optical and electrical properties. Graphene oxide is a chemically modified form of graphene in which the honeycomb lattice of carbon atoms is decorated with oxygen bearing functional groups. Graphene oxide represents a facile route for the production of large quantities of graphene based materials, is stable in aqueous and polar organic solvents and has the potential for further chemical modification. In this dissertation, the origin and influence of hierarchical structure on the mechanical properties of graphene oxide paper and graphene oxide paper based materials has been investigated. Free-standing papers derived from graphene oxide are of interest as structural materials due to their impressive mechanical properties. While studies have investigated the mechanical properties of graphene oxide papers, little is known about the formation mechanism. Using a series of flash-freezing experiments on graphene oxide papers undergoing formation, a stop-motion animation of the fabrication process was obtained. The results explain the origin of the hierarchical nature of graphene oxide papers and provide a method for the tailoring of graphene oxide based materials. An in depth study of fusion of graphene oxide papers demonstrates a simple single-step route for the fabrication of practical materials derived from graphene oxide papers. Fused papers retain the properties of constituent papers allowing for the fabrication of mechanical heterostructures that replicate the hierarchical nature of natural materials. The contribution of the hierarchical nature of graphene oxide papers to the mechanical properties was examined by comparing papers formed by two different mechanisms. The intermediate length scale structures were found to play a key role in yielding tough papers with high failure stress. Finally, efforts to investigate the microstructural mechanisms that govern the mechanical properties of graphene oxide papers by 3D printing of a tensile tester are detailed. It is intended to release the design of the tensile tester to the community in an effort to reduce cost and improve availability of lab equipment.
- Publication:
-
Ph.D. Thesis
- Pub Date:
- 2016
- Bibcode:
- 2016PhDT.........8N
- Keywords:
-
- Mechanical engineering;Materials science