Transport properties of the sodium-yttrium-silicate glasses
Abstract
The influence of yttrium oxide on the transport properties and chemical stability of sodium silicate glasses is investigated. The seven sodium-yttrium silicate glass compositions were synthesised. There are three composition with Na2O/Y2O3 = 6.5 and four with permanent Na2O content with 5 to 8 mol% of Y2O3. The thermal behaviour of the glasses was studied with dilatometric and DSC methods. The research into the electrical characteristics of the glass has shown that their electrical conductivity is in the range of 5 × 10- 8-10- 6 S/cm at 25 °C and 10- 3 S/cm at 300 °C. It is shown that the hydrolytic resistance increases when growing the Y2O3 concentration in the glass composition at constant Na2O content.
- Publication:
-
Journal of Non Crystalline Solids
- Pub Date:
- August 2016
- DOI:
- 10.1016/j.jnoncrysol.2016.04.044
- Bibcode:
- 2016JNCS..445...30N
- Keywords:
-
- Glassy solid electrolytes;
- Sodium-yttrium-silicate glass;
- The glass transition temperature;
- Crystallisation temperature;
- Conductivity;
- Basicity of glass