Magneto-structural transitions induced at 1.2 K in Ni2MnGa-based Heusler alloys by high magnetic field up to 60 T
Abstract
The huge decrease of the martensitic transition temperature T M-A with increasing field (up to dT M-A /dH = -8.1 K T-1) was observed in all the Co-doped and In-doped Ni50 - x Co x Mn25 + y Ga25 - y - z In z Heusler alloys at high pulse magnetic field up to 60 T. The structural martensitic transitions were induced at temperatures 2 K and 1.2 K in the Ni1.72Co0.28Mn1.25Ga0.75 and Ni1.65Co0.34Mn1.31Ga0.62In0.07 alloys, respectively. The transitions are accompanied by a significant increase of magnetization of their austenite phase with increasing field up to M A(2 K) = 6.3 μ B/f.u. The very slight increase of magnetization of their martensite phase M M(2 K) was induced by the high magnetic field in both, the stoichiometric Ni2MnGa and the off-stoichiometric Ni1.65Co0.34Mn1.31Ga0.62In0.07 alloys. The presented results demonstrate the key role of magnetism in the martensitic transitions in the Ni2MnGa based Heusler alloys and point to the Jahn-Teller effect as a source of the tetragonal distortion of crystal structure of these alloys.
- Publication:
-
Materials Research Express
- Pub Date:
- March 2014
- DOI:
- 10.1088/2053-1591/1/1/016109
- Bibcode:
- 2014MRE.....1a6109K