Fabrication and characterization of mesoporous activated carbon from Lemna minor using one-step H3PO4 activation for Pb(II) removal
Abstract
A low cost and locally available material, Lemna minor, was used to fabricate activated carbon using H3PO4 activation. After H3PO4 activation, the L. minor activated carbons (LACs) possess high mesoporosity (92.2%) and a surface area of 531.9 m2/g according to Brunauer-Emmett-Teller (BET) analysis. Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectrometer (XPS) analyses reveal the presence of rich hydroxyl, carboxyl, amide and phosphate functional groups on the LACs surface, leading to facile Pb(II) binding to the surface through strong chemisorptive bonds or ion-exchange. The kinetic and equilibrium data were well described by pseudo-first-order model and Langmuir isotherm, with the maximum monolayer adsorption capacity (qm) 170.9 mg/g at 25 °C. The intra-particle diffusion mechanism was partially responsible for the adsorption. The adsorption process was spontaneous and endothermic with negative ΔG and positive ΔH. The Pb(II)-loaded LACs could be easily regenerated using 0.1-M HCl and reused for seven cycles without significant adsorption capacity reduction. The maximum percentage removal rate for Pb(II) (20 mg/L) was found to be 91.8% within 30 min, at optimum conditions of pH 6.0 and 25 °C. These suggested that the low-cost LACs could be used as a potential adsorbent in the treatment of lead-contaminated water.
- Publication:
-
Applied Surface Science
- Pub Date:
- October 2014
- DOI:
- 10.1016/j.apsusc.2014.08.152
- Bibcode:
- 2014ApSS..317..422H
- Keywords:
-
- Lead;
- Activated carbon;
- Lemna minor;
- Mesoporous;
- Adsorption