Highly durable polymer electrolyte membranes at elevated temperature: Cross-linked copolymer structure consisting of poly(benzoxazine) and poly(benzimidazole)
Abstract
For polymer electrolyte membrane fuel cell (PEMFC) applications at elevated temperature (>100 °C), a series of cross-linked benzoxazine-benzimidazole copolymer, P(HFa-co-BI), membranes are prepared by casting a solution of poly[2,2‧-(m-phenylene)-5,5‧-bibenzimidazole] (PBI) and di-functional benzoxazine monomer, 6,6‧-(hexafluoroisopropylidene)bis(3-phenyl-3,4-dihydro-2H-benzoxazine) (HFa), in N,N-dimethylacetamide prior to stepwise heating to 250 °C. The films are also viable to manufacture to large quantities and area by roll-to-roll coating. The resulting cross-linked copolymer, P(HFa-co-BI), membranes are found to be thermally and mechanically stable. Although the proton conductivity values of P(HFa-co-BI) membranes are smaller than that of the PBI membrane, their cell performance (0.68 V at 0.2 A cm-2 at 150 °C) is close to that of PBI membrane and their long-term durability (ca. 3116 cycles on in situ accelerated lifetime mode of load cycling testing) is found to be far superior to the PBI membrane.
- Publication:
-
Journal of Power Sources
- Pub Date:
- March 2013
- DOI:
- 10.1016/j.jpowsour.2012.11.019
- Bibcode:
- 2013JPS...226..346K