Production of Ti-C presolar carbide grain analogies and its infrared spectra
Abstract
The infrared emission of the circumstellar environment of carbon-rich stars and dense molecular cloud cores is believed to be dominated by the emissivity of carbon dust. The origins of absorption peaks will be identified on the basis of laboratory studies. Important factors in the determination of absorption features are size, shape and structure of the grain (Bohren and Huffman, 1983). Therefore, the production of presolar grain analogy is important for the identification of the observation spectra.
Recently, we succeeded in the formation of Si-, Ti- and Zr-C grains of the order of 50 nm by advanced gas evaporation method. We have started to obtain characteristic data of carbide grains in laboratory experiments. The spectra from ultraviolet to infrared of samples embedded in KBr pellets are presented. In the present study, we will elucidate the correlation between the size of TiC grain or thickness of the carbon mantle layer and spectra of TiC core-carbon mantle grains. Because TiC is one of the candidates of 21 micron feature. The absorption peaks of TiC core (50 nm)-carbon mantle (2 nm) grains were found to be at 9.5 and 12.5 microns. When the thickness of the mantle layer increased to 15 nm, the peak at 12.5 microns disappeared and the peak at 9.5 microns was significantly weakened. These results are similar to the calculated result for SiC core-carbon mantle grains, i.e., increased thickness of the mantle layer weakens the spectrum intensity (Kozasa et al., 1996). The 20.1 micron absorption feature never appeared, even if the same size grains seen in meteorites were produced. Moreover, the infrared spectra were observed when the size of TiC grains was smaller than presolar grain. Carbon was deposited on the surface of Ti grains. Then, TiC nanocrystallites with the size of 2-3 nm were produced by the diffusion of Ti and/or carbon. The new absorption feature was appeared at 14 microns. The 12.5 micron absorption was hardly seen. If the samples are heated at 700circC for 1h, crystallites size of TiC was increased to about 5 nm. The absorption feature at 14 microns was weaken. It was concluded that the infrared absorption feature was depend on the crystallites size.- Publication:
-
Astrophysics of Dust
- Pub Date:
- 2003
- Bibcode:
- 2003asdu.confE.153K