Ion beam mixing and radiation enhanced diffusion in metal/ceramic interfaces
Abstract
Ion beam techniques are frequently used to modify the physical properties of materials. It is the aim of this contribution to obtain information on ion beam effects on irradiated metal/ceramic interfaces with bilayer geometry. Ion beam mixing and radiation enhanced diffusion have been investigated in Cu/Al2O3, Au/Al2O3 and Au/ZrO2 samples. Specimen, with thicknesses of the metallic film in the range of 60-70 nm, were prepared by vapor deposition and irradiated with 150 keV Ar+ ions in the range of 0.9 × 1016 to 1.5 × 1017 Ar+/cm2. Sample temperature during irradiation was varied between 77 K and 673 K. The mixing behaviour was analysed using concentration depth profiles measured by Rutherford Backscattering Spectroscopy (RBS). The results show that mixing efficiencies for all elements scale linear by the Ar+ ion dose. Radiation enhanced diffusion is separated from temperature independent mixing processes. High resolution scanning electron microscopy (HREM) showed strong surface deterioration for the Au/Al2O3 and Au/ZrO2 samples. X-Ray Photoelectron Spectroscopy (XPS) analysis in the particular case of the Cu/Al2O3 interface was performed.
- Publication:
-
Nuclear Instruments and Methods in Physics Research B
- Pub Date:
- December 1995
- Bibcode:
- 1995NIMPB.106..589B