Specific features of thermal and magnetic properties of Yb B50 at low temperatures
Abstract
Heat capacity, thermal expansion, and magnetization of ytterbium boride Yb B50 were studied at temperatures 0.6-300 K, 5-300 K, and 2-300 K, respectively. We revealed two smooth peaks at about 4.0 and 60 K in the temperature dependence of the heat capacity. A comparison with the heat capacity of the diamagnetic isostructural boride Lu B50 shows that these anomalies can be attributed to excitations in the ytterbium sublattice (Schottky anomalies). A scheme for splitting of the ground 7/2 2F multiplet of Y b3 + ions in the crystal field is proposed. Reliability of the proposed crystal-field energies of the Y b3 + ions is confirmed by the analysis of temperature dependencies of magnetic susceptibility and magnetization in applied magnetic fields up to 55 kOe. A clear anisotropy of the thermal expansion and a negative expansion within a wide temperature range (40-185 K) were observed. Assuming that this anomaly of the thermal expansion in higher borides is caused by the specific thermal evolution of a crystal lattice observed earlier, in particular, in Lu B50 , and the interaction of rare-earth ions with lattice strains, we have determined phenomenological Grüneisen parameters which characterize effects due to thermal transitions of Y b3 + ions between the ground and excited states. A phase transition of Yb B50 to any magnetically ordered state was not observed down to the lowest temperatures of experiments.
- Publication:
-
Physical Review Materials
- Pub Date:
- May 2018
- DOI:
- 10.1103/PhysRevMaterials.2.054401
- Bibcode:
- 2018PhRvM...2e4401N