Abstract
The effect of oxygen content on the glass forming ability of the Zr50Cu40Al10 alloy is presented. Two different oxygen levels, 194 ± 26 wt. ppm and 918 ± 72 wt. ppm, in the arc melted and suction cast alloys were obtained using Zr metal of different forms and nominal oxygen contents. Critical diameters for glass formation were determined by microstructural observations of cast conical and rod-shaped samples. Their structures were further investigated by X-ray diffraction. The critical diameter of the alloy with the lower oxygen content was 8 mm, while for the higher oxygen content it was below 3 mm. For the latter, the τ3 (Zr51Cu28Al21) crystalline inclusions were observed in the central part of the 3 mm diameter sample. The fully amorphous samples exhibited a large supercooled liquid range and a high reduced glass transition temperature.
- Publication:
-
Journal of Non Crystalline Solids
- Pub Date:
- September 2018
- DOI:
- 10.1016/j.jnoncrysol.2018.05.034
- Bibcode:
- 2018JNCS..496...42P
- Keywords:
-
- Bulk metallic glasses;
- Critical diameter;
- Oxygen content;
- Glass forming ability;
- Thermal stability;
- Zirconium