Evaluation of Delamination of X80 Pipeline Steel Coating Under Alternating Stray Current Via Scanning Electrochemical Microscopy
Abstract
The delamination of epoxy coating on X80 pipeline steel was evaluated under various stray alternating current (AC) interferences (0-300 A/m2). Qualitative and quantitative analyses were carried out using scanning electrochemical microscopy (SECM), electrochemical impedance spectroscopy (EIS), and three-dimensional digital microscopy. The results show that the SECM current is directly proportional to the soaking time and applied current density. The variation in SECM current curve shape indicates the delamination distance of epoxy coatings at the defect area. The depths of corrosion pits at 50, 100, and 300 A/m2 stray currents were 140, 160, and 240 μm, respectively. The corrosion pits also became wider with increasing current densities. With increasing stray AC densities, both the coating delamination and pit depth became more severe at the same soaking time. The EIS results show that the change in impedance was not significant without stray current, whereas the impedance first decreased and then increased when stray current was applied. These results are consistent with the SECM measurements.
- Publication:
-
Journal of Materials Engineering and Performance
- Pub Date:
- June 2018
- DOI:
- 10.1007/s11665-018-3365-z
- Bibcode:
- 2018JMEP...27.3060W
- Keywords:
-
- coating delamination;
- stray current;
- scanning electrochemical microscopy;
- electrochemistry;
- corrosion morphology;
- X80 pipeline steel