Structural, Electrical and Magnetic Properties in the System {Na}_{0.5} {CoO}_{3} Na 0.5 CoO 3
Abstract
The present study reports the structural, magnetic and electrical properties of the Na_{0.5}CoO3 system produced by the conventional solid state reaction method. The X-ray diffraction analysis allows to infer that the compound crystallizes in a monoclinic system with spatial group it{C2/m} and network parameters: a = 5.55 (8) Å, b = 4.87 (3) Å y c = 2.85 (8) Å. It is found that the mean grain size of the stoichiometric of system amounts approximately to 76 nm. Below 40 K, an antiferromagnetic behavior with {T}_{N }≈ 40 K was observed, while in the region between 80 and 190 K the system obeys the law of Curie-Weiss, and the effective magnetic moment was determined experimentally of 5.62{μ }B, indicating a high spin configuration for the Co^{2+ }ion ( S = 3/2) in the fundamental state 4T_{1g}. The system shows cluster spin glass properties with low temperatures, the temperature of magnetic moment freezing from ∼ 40 K. The behavior of the resistivity under absence of magnetic field and the presence of an insulating state between two different metallic states was observed. The metal-insulator transition occurred at two temperatures, the first around 170 K, and the second around 40 K, the latter in accordance with the magnetic transition temperature.
- Publication:
-
Journal of Low Temperature Physics
- Pub Date:
- March 2018
- DOI:
- 10.1007/s10909-017-1841-8
- Bibcode:
- 2018JLTP..190..267E
- Keywords:
-
- Moment magnetic;
- Antiferromagnetic;
- High spin;
- Metal-insulation transition