Surface Morphologies of Ti and Ti-Al-V Bombarded by 1.0-MeV Au+ Ions
Abstract
Ion implantation is known to enhance the mechanical properties of biomaterials such as, e.g., the wear resistance of orthopedic joints. Increasing the surface area of implants may likewise improve their integration with, e.g., bone tissue, which requires surface features with sizes in the micron range. Ion implantation of biocompatible metals has recently been demonstrated to induce surface ripples with wavelengths of a few microns. However, the physical mechanisms controlling the formation and characteristics of these patterns are yet to be understood. We bombard Ti and Ti-6Al-4V surfaces with 1.0-MeV Au+ ions. Analysis by scanning electron and atomic force microscopies shows the formation of surface ripples with typical dimensions in the micron range, with potential indeed for biomedical applications. Under the present specific experimental conditions, the ripple properties are seen to strongly depend on the fluence of the implanted ions while being weakly dependent on the target material. Moreover, by examining experiments performed for incidence angle values θ =8 ° , 23°, 49°, and 67°, we confirm the existence of a threshold incidence angle for (ripple) pattern formation. Surface indentation is also used to study surface features under additional values of θ , agreeing with our single-angle experiments. All properties of the surface structuring process are very similar to those found in the production of surface nanopatterns under low-energy ion bombardment of semiconductor targets, in which the stopping power is dominated by nuclear contributions, as in our experiments. We consider a continuum model that combines the effects of various physical processes as originally developed in that context, with parameters that we estimate under a binary-collision approximation. Notably, reasonable agreement with our experimental observations is achieved, even under our high-energy conditions. Accordingly, in our system, ripple formation is determined by mass-redistribution currents reinforced by ion-implantation effects, which compete with an unstable curvature dependence of the sputtering yield.
- Publication:
-
Physical Review Applied
- Pub Date:
- December 2017
- DOI:
- 10.1103/PhysRevApplied.8.064027
- Bibcode:
- 2017PhRvP...8f4027G