Characterization of Briquette from the Corncob Charcoal and Sago Stem Alloys

The briquettes fabricated from charcoal of corncob (zea mays,L) and sago stem (metroxilon sago rottb) have been produced and characterized. The samples were prepared step by step carefully. The charcoal powder filtered by strainer with mesh size of 70-80 to get the homogeneous particle size. Briquettes are made by mixing corncob charcoal powder, sago stem charcoal and sago adhesive with a mass ratio of 4:5:1, 4.5: 4.5: 1, 5:4:1. The materials are mixed with hot water and stirred to get homogeneous blend. Then they are compacted by pressure of 34.66kg/cm², 69.32kg/cm2, and 103.98kg/cm² to form a cylindrical shape with diameter of 4 cm. The cylindrical briquettes then were dried at temperature of 60°C for 48 hours. After dried, the samples where then characterized their density and water, ash, volatile matter, fixed carbon contents. The burning rate, combustion temperature, and ignition time were also determined. The experimental results show that the briquettes have average densities from 0.602 to 0.717gr/cm³. The density increase with the increasing of forming pressure. The increasing of pressure also result in the decreasing of moisture content from 2.669% to 0.842%. The ash content is found from 3.459% to 8.766%. Volatile matter and fixed carbon are varies from 13.658% and 21.168% and 67.667% to 80.758% respectively. The lowest burning rate is 0.0898gr/s and the optimum burning temperature is 499.2°C with the lowest ignition time of 1.58 minutes. These briquette’s parameters agree wit the quality standard of industrial briquette.