Carbon dioxide capture using Sodium bicarbonate/Sodium carbonate supported on nanoporous Iron(III) oxide

Strong evidence exists suggesting that anthropogenic emissions of CO 2, primarily from the combustion of fossil fuels, have been contributing to global climate change, including warming of the atmosphere and acidification of the oceans. These, in turn, lead to other effects such as melting of ice and snow cover, rising sea levels, severe weather patterns, and extinction of life forms. With these detrimental shifts in ecosystems already being observed, it becomes imperative to mitigate anthropogenic CO2. CO2 capture is typically a costly operation, usually due to the energy required for regeneration of the capture medium. Na2CO3 is one potential capture medium with the potential to decrease this energy requirement. Extensively researched as a potential sorbent for CO2, Na2CO3 is well known for its theoretically low energy requirement, due largely to its relatively low heat of reaction compared to other capture technologies. Its primary pitfalls, however, are its extremely low reaction rate during sorption and slow regeneration of Na2CO 3. Before Na2CO3 can be used as a CO2 sorbent, then, it is critical to increase its reaction rate. In order to do so, this project studied nanoporous FeOOH as a potential supporting material for Na2CO3. Because regeneration of the sorbent is the most energy-intensive step when using Na2CO3 for CO 2 sorption, this project focused on the decomposition of NaHCO 3, which is equivalent to CO2 desorption. Using BET, FTIR, XRD, XPS, SEM, TEM, magnetic susceptibility tests, and Mossbauer spectroscopy, we show FeOOH to be thermally stable both with and without the presence of NaHCO3 at temperatures necessary for sorption and regeneration, up to about 200°C. More significantly, we observe that FeOOH not only increases the surface area of NaHCO3, but also has a catalytic effect on the decomposition of NaHCO3, reducing activation energy from 80 kJ/mol to 44 kJ/mol. This reduction in activation energy leads to a significant increase in the reaction rate by a factor of nearly 50, which could translate into a substantial decrease in the cost of using Na2 CO3 for CO2 capture.