Evolution of the mechanical properties and microstructure of ferritic-martensitic steels irradiated in the BOR-60 reactor
Abstract
The effect of neutron irradiation on mechanical properties of low-activation ferritic-martensitic (FM) steels 0.1C-9Cr-1W, V, Ta, B and 0.1C-12Cr-2W, V, Ti, B is studied under tension at temperatures of 330-540 °C and doses of 50 dpa. Steel 0.1C-13Cr-Mo, V, Nb, B was chosen for comparison. At irradiation temperatures of 330-340 °C, the radiation hardening of steel with 9%Cr achieves saturation at a dose of 10 dpa. In this case as compared to steels with 12%Cr, the fracture surface is characterized as ductile without cleavage traces. At irradiation temperatures higher than 420 °C, there is no difference in the behavior of the materials under investigation. The data on radiation creep obtained by direct measurement and from the profilometry data satisfy a model ɛ¯/ σ¯=B 0+D Ṡ, when B0 and D have the values typical for steels of FM type.
- Publication:
-
Journal of Nuclear Materials
- Pub Date:
- December 2002
- DOI:
- 10.1016/S0022-3115(02)01179-0
- Bibcode:
- 2002JNuM..307..229S