poly-methyltrioxorhenium {(CH3)0.92ReO3}∞ : A conducting two-dimensional organometallic oxide

Polymeric methyltrioxorhenium, {(CH₃)_0.92ReO₃}_∞ (poly-MTO), is a prominent member of the organometallic hybrids which adopts the structural pattern and physical properties of classical perovskites in two dimensions (2D). We demonstrate how the electronic structure of poly-MTO can be tailored by an intercalation of organic donor molecules, such as tetrathiafulvalene (TTF) or bis-(ethylendithio)-tetrathiafulvalene (BEDT-TTF), and by the inorganic acceptor SbF₃ . The integration of donor molecules leads to a more insulating behavior of poly-MTO, whereas the SbF₃ insertion does not cause any significant change in the resistivity. In particular, with increasing donor intercalation the metallic behavior of the parent compound, poly-MTO, becomes surprisingly suppressed leading to an insulator at TTF (BEDT-TTF) donor concentrations above 50% (25%). The resistivity data of pure poly-MTO exhibit a crossover from metallic (dρ/dT>0) to insulating (dρ/dT>0) behavior at a characteristic temperature around T_min≃38K . Above T_min the resistivity ρ(T) is remarkably well described by a two-dimensional electron system. Below T_min an unusual resistivity behavior, similar to that found in doped cuprates, is observed: The resistivity initially increases approximately as ρ∼ln(1/T) before it changes into a T dependence below 2K . As an explanation we suggest a crossover from purely two-dimensional charge-carrier diffusion within the {ReO₂}_∞ planes at high temperatures to three-dimensional diffusion at low temperatures in a disorder-enhanced electron-electron interaction scenario (Altshuler-Aronov correction). Furthermore, a linear positive magnetoresistance was found in the insulating regime, which is caused by spatial localization of itinerant electrons at some of the Re atoms, which formally adopt a 5d¹ electronic configuration. X-ray diffraction, IR, and ESR studies, temperature dependent magnetization, and specific heat measurements in various magnetic fields suggest that the electronic structure of poly-MTO can safely be approximated by a purely 2D conductor which is labile towards spatial localization of electrons under the formation of Re(d¹) centers in the presence of a magnetic field.