Characterization of transport and magnetic properties in thin film La0.67(CaxSr1-x)0.33MnO3 mixtures
Abstract
We have grown thin films of (100)-oriented La0.67(CaxSr1-x)0.33MnO3 on (100) NdGaO3 substrates by off-axis sputtering. We have looked at the changes in the resistivity and magnetoresistance of the samples as the Ca/Sr ratio was varied. We find that as the calcium fraction is decreased, the lattice match to the substrate decreases, and the films become more disordered, as observed in transport measurements and the variation in Curie and peak resistance temperatures. We find a correlation between the temperature independent and T2 terms to the low temperature resistivity. The room temperature magnetoresistance exhibits a maximum as the peak temperature is increased by the substitution of Sr for Ca, and a change in the field dependence to the resistivity at room temperature is observed.
- Publication:
-
Journal of Applied Physics
- Pub Date:
- May 1999
- DOI:
- 10.1063/1.370162
- arXiv:
- arXiv:cond-mat/9902020
- Bibcode:
- 1999JAP....85.6563B
- Keywords:
-
- 75.70.Pa;
- 75.60.Ej;
- 75.30.Vn;
- 73.61.-r;
- Magnetization curves hysteresis Barkhausen and related effects;
- Electrical properties of specific thin films;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- 5 pages, 6 eps figures, to be published in Journal of Applied Physics