Spontaneous ordering in (Zn,Be)Se: A vibrational study by Raman scattering and first-principles calculations

Spontaneous ordering in Zn(1-x)Be(x)Se (0<x<0.92) is identified from transverse optical Raman spectra as a slight but systematic reinforcement of low-frequency Be-Se mode, that refers to the `longer' bonds from the Be-rich region, to the detriment of the high-frequency Be-Se counterpart, due to the `shorter' bonds from the Zn-rich region. The underlying mechanism of local Zn and Be segregation into a series of alternating cationic planes is explained. Direct insight upon the critical value of the order parameter Eta corresponding to `full condensation' of the original 1-bond->2-mode (phonon, bond length) situation onto the optimum 1-bond->1-mode end situation that minimizes the local strain energy in the representative ZnBeSe2 system (x=0.5) is achieved via first-principles bond length/phonon calculations in a series of fully relaxed Zn(8)Be(8)Se(16) supercells with Eta ranging from 0 (random alloy) to 1 (CuPt-type ordering). `Full condensation' is achieved at Eta=0.5. In case of further ordering, the alloy would be forced to re-adopt non-optimum 1-bond->2-mode type behavior, the result of the formation of ZnSe/BeSe microdomains. Eta=0.5 appears as an intrinsic limit to SO in ZnBeSe2, and possibly in stoichiometric alloys in general.