Ion beam induced modification of exchange interaction and spin orbit coupling in the Co2FeSi Heusler compound
Abstract
A Co2FeSi (CFS) film with L21 structure was irradiated with different fluences of 30 keV Ga+ ions. Structural modifications were subsequently studied using the longitudinal (LMOKE) and quadratic (QMOKE) magneto-optical Kerr effect. Both the coercivity and the LMOKE amplitude were found to show a similar behaviour upon irradiation: they are nearly constant up to ion fluences of ap6 × 1015 ion cm-2, while they decrease with further increasing fluences and finally vanish at a fluence of ap9 × 1016 ion cm-2, when the sample becomes paramagnetic. However, contrary to this behaviour, the QMOKE signal nearly vanishes even for the smallest applied fluence of 3 × 1014 ion cm-2. We attribute this reduction of the QMOKE signal to an irradiation-induced degeneration of second or higher order spin-orbit coupling, which already happens at small fluences of 30 keV Ga+ ions. On the other hand, the reduction of coercivity and LMOKE signal with high ion fluences is probably caused by a reduction of the exchange interaction within the film material.
- Publication:
-
Journal of Physics D Applied Physics
- Pub Date:
- March 2007
- DOI:
- 10.1088/0022-3727/40/6/S08
- arXiv:
- arXiv:cond-mat/0609633
- Bibcode:
- 2007JPhD...40.1558H
- Keywords:
-
- Condensed Matter - Materials Science
- E-Print:
- doi:10.1088/0022-3727/40/6/S08