Fluxoid jump coupled high critical current density of nano-Co3O4 doped MgB2
Abstract
Polycrystalline MgB2 samples, with added 0, 2, 4 and 6% nano-Co3O4, synthesized by vacuum (10-5 Torr) annealing at 750 °C for two and a half hours each, are found to be nearly single phase with the presence of only a small quantity of Mg/MgO in the pristine sample in addition to the Co2O3 in the doped compounds. All the samples exhibited clear and sharp diamagnetic transitions at around 38 K, in zero-field-cooled (ZFC) magnetic susceptibility measurements with a sizeable signal. The field-cooled (FC) measurements, though having sharp transitions, showed a very small signal, indicating a high level of pinning centres in these samples. Further, some of the doped samples exhibited the paramagnetic Meissner effect (PME) in an applied field of 5 Oe. The critical current density (Jc), estimated by invoking Bean's model for the pristine compound, increases by nearly an order of magnitude for 2% and 4% nano-Co3O4 doping and then decreases sharply for the 6% sample at nearly all studied temperatures and applied fields. Further, the increased Jc (~108 A cm-2) is coupled with fluxoid jumps (T<=20 K and H<=1 T). Fluxoid jumps are not seen in the relatively low Jc pristine or 6% sample. This means that the fluxoid jumps are intrinsic only to the high-Jc samples.
- Publication:
-
Superconductor Science Technology
- Pub Date:
- June 2006
- DOI:
- 10.1088/0953-2048/19/6/023
- arXiv:
- arXiv:cond-mat/0601359
- Bibcode:
- 2006SuScT..19..551A
- Keywords:
-
- Condensed Matter - Superconductivity;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- 14 pages including TEXT + Figs. Comments Welcome (AWANA.Veer@nims.go.jp) OR awana@mail.nplindia.ernet.in