Polar Domains in Lead Titanate Films under Tensile Strain
Abstract
Thin films of PbTiO3, a classical ferroelectric, have been grown under tensile strain on single-crystal substrates of DyScO3. The films, of only 5 nm thickness, grow fully coherent with the substrate, as evidenced by synchrotron x-ray diffraction. A mapping of the reciprocal space reveals intensity modulations (satellites) due to regularly spaced polar domains in which the polarization appears rotated away from the substrate normal, characterizing a low-symmetry phase not observed in the bulk material. This could have important practical implications since these phases are known to be responsible for ultrahigh piezoelectric responses in complex systems.
- Publication:
-
Physical Review Letters
- Pub Date:
- March 2006
- DOI:
- 10.1103/PhysRevLett.96.127602
- arXiv:
- arXiv:cond-mat/0512632
- Bibcode:
- 2006PhRvL..96l7602C
- Keywords:
-
- 77.55.+f;
- 61.10.-i;
- 68.55.-a;
- 77.80.-e;
- Dielectric thin films;
- X-ray diffraction and scattering;
- Thin film structure and morphology;
- Ferroelectricity and antiferroelectricity;
- Condensed Matter - Materials Science
- E-Print:
- Nature of changes: Slightly modified abstract, introduction and conclusion paragraphs to make it more accessible to the general reader. Corrected a typo in the value of the domain period. These changes do not affect the content and results. To be published in PRL