Optimizing Tc in the (Mn,Cr,Ga)As and (Mn,Ga)(As,P) ternary alloys

We explore two possible ways to enhance the critical temperature T_c in the dilute magnetic semiconductor Mn_0.08Ga_0.92As. Within the context of the double-exchange and RKKY pictures, the ternary alloys Mn_xCr_0.08-xGa_0.92As and Mn_0.08Ga_0.92As_yP_1-y might be expected to have T_c higher than the pseudobinary Mn_0.08Ga_0.92As. To test whether the expectations from model pictures are confirmed, we employ linear response theory within the local-density approximation to search for theoretically higher critical temperatures in these ternary alloys. Our results show that neither co-doping Mn with Cr, nor alloying As with P improves T_c. Alloying with Cr is found to be deleterious to the T_c. Mn_0.08Ga_0.92As_yP_1-y shows almost linear dependence of T_c on y.