Structure-dependent microwave dielectric properties of (1-x)La(Mg1/2Ti1/2)O3-xLa2/3TiO3 ceramics

Structure and dielectric characterizations were performed on the (1-x)La(Mg_1/2Ti_1/2)O₃-xLa_2/3TiO₃ perovskite ceramics with the actual composition 0⩽x⩽0.52. The sequence of structure transformations was detected as x is increased: P₂₁/n(0⩽x <0.3)→Pnma(0.3⩽x<0.37)→Imma(0.37⩽x<0.4)→I2/a(0.4⩽x⩽0.49)→R3¯c(0.49<x⩽0.52). The structure evolution from the tilt configuration a^-b⁺a^- to a^-a^-a^- is considered in terms of competing the repulsive energy and the Madelung energy. Relative permittivity of the ceramics was measured as a function of temperature and La_2/3TiO₃ content. The temperature coefficient of the resonant frequency was found to pass zero value at the narrow compositional range between x =0.49 and 0.52, where the discontinuous I2/a →R3¯c crossover occurs. The temperature and compositional variations of these fundamental microwave dielectric parameters are discussed in respect to the type of the phase transitions (continuous/discontinuous) between the structures.