Neutron diffraction study of average and local structure in La0.5 Ca0.5 Mn O3

We used neutron powder diffraction to obtain the local and long-range structure of La_0.5Ca_0.5MnO₃ at room temperature and 20K . By combining Rietveld and pair distribution function analysis of the total neutron scattering data, we have analyzed the structure of the compound using two competing models describing the low temperature phase: first the charge-ordered-orbital-ordered model and second the MnMn dimer model. These structural models fit the 20K neutron powder diffraction pattern equally well using a Rietveld analysis. Therefore, pair distribution function analysis is used to probe the local and medium-range structure revealing a system with two distinctly distorted Mn octahedra and Mn ions with nonintegral valence states. The distorted octahedra differ with the structural model for the Zener polaron-type MnMn dimer picture proposed for Pr_0.60Ca_0.40MnO₃ and order in a similar checkerboard configuration associated with the CE-type antiferromagnetic structure. Therefore, locally the charge difference and structural ordering between the two Mn is appreciable enough to describe the system at 20K as “partially charge ordered.”