Superconductivity in MgB 2 doped with Ti and C

Measurements of the superconducting upper critical field, H_c2, and critical current density, J_c, have been carried out for MgB ₂ doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron on the MgB ₂ lattice and apparently shortens the electronic mean free path of MgB ₂ and raising H_c2. Titanium forms precipitates of either TiB or TiB ₂ that enhance the flux pinning and raise J_c. Most of these precipitates are intra-granular in the MgB ₂ phase. For samples containing both C and Ti doping, the C appears to still replace B in the MgB ₂ lattice and the Ti precipitates out as a boride. If approximately 0.5%Ti and approximately 2%C are co-deposited with B to form doped boron fibers and these fibers are in turn reacted in Mg vapor to form doped MgB ₂, the resulting superconductor has μ₀H_c2( T = 0) ∼ 25 T and J_c ∼ 10,000 A/cm ² at 5 K and 2.2 T.