Microwave magnetoelectric effects in single crystal bilayers of yttrium iron garnet and lead magnesium niobate-lead titanate
Abstract
The first observation of microwave magnetoelectric (ME) interactions through ferromagnetic resonance (FMR) in bilayers of single crystal ferromagnetic-piezoelectric oxides and a theoretical model for the effect are presented. An electric field E produces a mechanical deformation in the piezoelectric phase, resulting in a shift δHE in the resonance field for the ferromagnet. The strength of ME coupling is obtained from data on δHE vs E . Studies were performed at 9.3GHz on bilayers of (111) yttrium iron garnet (YIG) films and (001) lead magnesium niobate-lead titanate (PMN-PT). The samples were positioned outside a TE102 -reflection type cavity. Resonance profiles were obtained for E=0-8kV/cm for both in-plane and out-of-plane magnetic fields H . Important results are as follows. (i) The ME coupling in the bilayers is an order of magnitude stronger than in polycrystalline composites and is in the range 1-5.4Oecm/kOe , depending on the YIG film thickness. (ii) The coupling strength is dependent on the magnetic field orientation and is higher for out-of-plane H than for in-plane H . (iii) Estimated ME constant and its dependence on volume ratio for the two phases are in good agreement with the data.
- Publication:
-
Physical Review B
- Pub Date:
- August 2004
- DOI:
- 10.1103/PhysRevB.70.064416
- arXiv:
- arXiv:cond-mat/0405622
- Bibcode:
- 2004PhRvB..70f4416S
- Keywords:
-
- 75.80.+q;
- 75.50.Gg;
- 75.60.-d;
- 77.65.-j;
- Magnetomechanical and magnetoelectric effects magnetostriction;
- Ferrimagnetics;
- Domain effects magnetization curves and hysteresis;
- Piezoelectricity and electromechanical effects;
- Condensed Matter - Materials Science
- E-Print:
- To be published in Physical Review B