Magnetization and magnetotransport of LBa Co2 O5.5 (L=Gd,Eu) single crystals
Abstract
The magnetization, resistivity, and magnetoresistance (MR) of single crystals of GdBaCo2O5.5 and EuBaCo2O5.5 are measured over a wide range of dc magnetic fields (up to 30T ) and temperature. In LBaCo2O5.5 (L=Gd,Eu) , the Co ions are trivalent and can exist in three spin states, namely, the S=0 low-spin (LS) state, the S=1 intermediate-spin (IS) state, and the S=2 high-spin (HS) state. We confirm that GdBaCo2O5.5 and EuBaCo2O5.5 have a metal-insulator transition accompanied by a spin-state transition at TMI≈365 and 335K respectively. The data suggest an equal ratio of LS (S=0) and IS (S=1) Co3+ ions below TMI , with no indication of additional spin state transitions. The low-field magnetization shows a transition to a highly anisotropic ferromagnetic phase at 270K , followed by another magnetic transition to an antiferromagnetic phase at a slightly lower temperature. The magnetization data are suggestive of weak correlations between the Gd spins but no clear signature of ordering is seen for T>2K . Significant anisotropy between the a-b plane and c axis was observed in magnetic and magnetotransport properties for both compounds. For GdBaCo2O5.5 , the resistivity and MR data imply a strong correlation between the spin-order and charge carriers. For EuBaCo2O5.5 , the magnetic phase diagram is very similar to its Gd counterpart, but the low- T MR with current flow in the a-b plane is positive rather than negative as for Gd. The magnitude and the hysteresis of the MR for EuBaCo2O5.5 decrease with increasing temperature, and at higher T the MR changes sign and becomes negative. The difference in the behavior of both compounds may arise from a small valence admixture in the nonmagnetic Eu ions, i.e., a valence slightly less than 3+ .
- Publication:
-
Physical Review B
- Pub Date:
- July 2004
- DOI:
- 10.1103/PhysRevB.70.024425
- arXiv:
- arXiv:cond-mat/0405596
- Bibcode:
- 2004PhRvB..70b4425Z
- Keywords:
-
- 75.50.Dd;
- 75.30.Cr;
- 75.30.Gw;
- Nonmetallic ferromagnetic materials;
- Saturation moments and magnetic susceptibilities;
- Magnetic anisotropy;
- Condensed Matter - Strongly Correlated Electrons
- E-Print:
- Accepted for publication in PRB