Self-Affine Surface Morphology of Plastically Deformed Metals

We analyze the surface morphology of metals after plastic deformation over a range of scales from 10nm to 2mm using atomic force microscopy and scanning white-light interferometry. We demonstrate that an initially smooth surface during deformation develops self-affine roughness over almost 4 orders of magnitude in scale. The Hurst exponent H of one-dimensional surface profiles initially decreases with increasing strain and then stabilizes at H≈0.75. We show that the profiles can be mathematically modeled as graphs of a fractional Brownian motion. Our findings can be understood in terms of a fractal distribution of plastic strain within the deformed samples.