Structural and electrical properties of c-axis oriented Y 1- xCa xBa 2(Cu 1- yZn y) 3O 7- δ thin films grown by pulsed laser deposition

Ca- and Zn-subsituted Y _{1- x}Ca _xBa ₂(Cu _{1- y}Zn _y) ₃O _{7- δ} ( x=0, 0.05 and y=0, 0.02, 0.04, 0.05) thin films were grown on SrTiO ₃(1 0 0) substrates using the pulsed laser deposition (PLD) technique. Effects of various growth parameters on the quality of the film were studied via X-ray diffraction (XRD), atomic force microscopy (AFM), and in-plane resistivity, ρ_ab( T), measurements. The deposition temperature and oxygen partial pressure were gradually increased to 820 °C and 1.20 mbar, respectively. Films grown under these conditions exhibited good c-axis orientation (primarily limited by the grain size) and low values of the extrapolated residual resistivity, ρ(0), at zero temperature. The planar hole content, p, was determined from the room-temperature thermopower, S[290 K], measurements and the effects of oxygen annealing were also studied. Fully oxygenated samples were found to be overdoped with p∼0.195. The superconducting transition temperature T_c( p), and ρ( T, p) showed the expected systematic variations with changing Zn content.