Magnetism and Superconductivity in RuM 1.5Ce 0.5Sr 2Cu 2O 10 (M=Eu and Y)

RuY _1.5Ce _0.5Sr ₂Cu ₂O ₁₀, is not superconducting (SC) and orders magnetically at T_M=152 K. The Ru moment at 5 K is 0.75 μ_B. Ferromagnetic hysteresis loops are observed below T_irr=100 K. At 100 K, the remanent magnetization ( M_rem) and the coercive field ( H_C) become zero. Surprisingly, at T_irr< T< T_M a reappearance of antiferromagnetic (AFM) hysteresis loops are observed with a peak at 120 K for both M_rem and H_C. The paramagnetic constants are: P_eff=2.06 μ_B (greater than the 1.73 μ_B expected for low spin Ru ⁵⁺) and θ=136 K which agrees well with T_M. Substitution of Zn (2.5% atm.) for Cu in RuEu _1.5Ce _0.5 Sr ₂Cu ₂O ₁₀ ( T_C=38 K), suppresses T_C but does not affect the magnetic features such as: T_M and T_irr, M_rem and H_C. This indicates that both SC and magnetic states are practically decoupled. We argue that the magnetic structure of this system becomes (i) AFM ordered at T_M. (ii) Due to the tilting of the RuO ₆ octahedra away from the crystallographic c-axis, at T_irr< T_M, weak-ferromagnetic (W-FM) order is induced by the canting of the Ru moments. (iii) At T_C ( T_M/ T_C∼4), the specific materials (M=Eu, Gd) become SC. Below T_C, both SC and W-FM states coexist.