Titanium additions to MgB 2 conductors

A series of doping experiments are reported for MgB ₂ conductors that have been synthesized using doped boron fibers prepared by chemical vapor deposition (CVD) methods. Undoped MgB ₂ samples prepared from CVD prepared fibers consistently give critical current densities, J_c, in the range of 500,000 A/cm ² in low field at 5 K. These values fall by a factor of about 100 as the magnetic field increases to 3 T. For heavily Ti-doped boron fibers where the B/Ti ratio is comparable to 1, there is a substantial suppression of both T_c, superconducting volume fraction, and J_c values. If, however, a sample with a few percent Ti in B is deposited on a carbon substrate and reacted at 1100 °C, then T_c is suppressed only a couple of degrees and critical current densities are found to be J_c ∼ 2-5 × 10 ⁶ A/cm ² for superconducting layers ranging from 4 to 10 μm thick. These materials show J_c values over 10,000 A/cm ² at 25 K and 1.3 T.