Semiconductive and photoconductive properties of the single-molecule magnets Mn12-acetate and Fe8Br8

Resistivity measurements are reported for single crystals of Mn₁₂-acetate and Fe₈Br₈. Both materials exhibit a semiconductor-like, thermally activated behavior over the 200 300 K range. The activation energy E_a obtained for Mn₁₂-acetate was 0.37±0.05 eV, which is to be contrasted with the value of 0.55 eV deduced from the earlier reported absorption edge measurements and the range of 0.3 1 eV from intramolecular density of states calculations, assuming 2E_a=E_g, the optical band gap. For Fe₈Br₈, E_a was measured as 0.73±0.1 eV, and is discussed in light of the available approximate band structure calculations. Some plausible pathways are indicated based on the crystal structures of both lattices. For Mn₁₂-acetate, we also measured photoconductivity in the visible range; the conductivity increased by a factor of about 8 on increasing the photon energy from 632.8 nm (red) to 488 nm (blue). X-ray irradiation increased the resistivity, but E_a was insensitive to exposure.