Doping phase diagram of Y1-xCaxBa2(Cu1-yZny)3O7-δ from transport measurements: Tracking the pseudogap below Tc

The effects of planar hole concentration, p , and magnetic field on the resistivity, ρ(T) , of high-quality c -axis oriented crystalline thin films and sintered Y_1-xCa_xBa₂(Cu_1-yZn_y)₃O_7-δ samples were investigated over a wide range of Ca, Zn, and oxygen contents. Zn was used to suppress superconductivity and this enabled us to extract the characteristic pseudogap temperature, T*(p) below T_c0(p)[≡T_c(x=0,y=0)] . We have also located the characteristic temperature, T_scf , marking the onset of significant superconducting fluctuations above T_c , from the analysis of ρ(T,H,p) and ρ(T,p) data. From this we are able to identify T*(p) near the optimum doping level where the values of T*(p) and T_scf(p) are very close and hard to distinguish. We again found that T*(p) depends only on the hole concentration p , and not on the level of disorder associated with Zn or Ca substitutions. We conclude that (i) T*(p) (and therefore, the pseudogap) persists below T_c0(p) on the overdoped side and does not merge with the T_c0(p) line and (ii) T*(p) and the pseudogap energy extrapolate to zero at the doping p=0.19±0.01 .