Crystal chemistry of carbon-substituted MgB 2

Neutron powder diffraction has been used to characterize a sample of C-substituted MgB ₂ synthesized from Mg and B ₄C (with isotopically enriched ¹¹B). The sample is multiphase, with the major phase [73.4(1) wt%] being Mg(B _{1- x}C _x) ₂ with x=0.10(2). Minor phases include MgB ₂C ₂, Mg, and MgO. The major Mg(B _{1- x}C _x) ₂ phase displays diffraction peak widths as sharp as for pure MgB ₂, indicating good C homogeneity. There is no evidence for ordering of the substituted C atoms or distortion of the host structure other than contraction of the a axis and slight expansion of the c axis. The observed changes in lattice parameters vs. C concentration provide a means for estimating the C concentration in other Mg(B _{1- x}C _x) ₂ samples. The reduction in T_c resulting from 10% C substitution is much larger than previously reported, suggesting that previous reports of the C concentration in Mg(B _{1- x}C _x) ₂ are overestimated. The Mg site occupancy is determined to be 0.990(4) which is consistent with full Mg occupancy. Given these results, the stoichiometry Mg(B _0.9C _0.1) ₂ should be used by future attempts (band structural or otherwise) to explain (i) the dramatic suppression of T_c ( T_c≈22 K) and (ii) the persistence of the two-superconducting-gap feature in the specific heat data.