Magneto-superconductivity of 100-atm O 2-annealed RuSr 2Gd 1.5Ce 0.5Cu 2O 10- δ

Studied 100-atm O ₂-annealed RuSr ₂Gd _1.5Ce _0.5Cu ₂O _{10- δ} (Ru-1222) compound crystallized in a tetragonal I4/mmm space group crystal structure. Thermo-gravimetric (TG) analysis was successfully applied to establish the oxygen content of the sample studied at 9.63 per formula unit. The DC magnetization data ( M vs. T) revealed magnetic transition at ∼100 K followed by superconducting transition at ∼40 K. Low field (-100⩽ H⩽100 Oe) M vs. H hysteresis loop showed a lower critical field ( H_c1) value of around 25 Oe. Ferromagnetic component is evidenced at 5, 10, 20 and 40 K. Near saturation field of above 5 T is observed at 5 K. Zero-field returning moment ( M_r) and zero-moment coercive field ( H_c) values at 5 K are 0.35 μ_B and 250 Oe. The resistance vs. temperature ( R vs. T) behaviour of the sample confirmed superconductivity at around 43 K. Superconductivity transition ( T_c) is broadened under magnetic field with strong granularity like steps.