High dielectric permittivity in AFe1/2B1/2O3 nonferroelectric perovskite ceramics (A=Ba, Sr, Ca; B=Nb, Ta, Sb)

AFe_1/2B_1/2O₃(A=Ba, Sr, Ca; B=Nb, Ta, Sb) ceramics were synthesized and temperature dependences of dielectric permittivity were measured at different frequencies. The experimental data obtained show very high values of dielectric permittivity in a wide temperature interval that is inherent to so-called high-k materials. Analyses of these data establish a Maxwell-Wagner mechanism as a main source for the phenomenon observed.