High transport critical current density obtained for powder-in-tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
Abstract
MgB2 tapes and wires were fabricated by the powder-in-tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density Jc of about 10 000 A/cm2 at 4.2 K and 5 T. A high Jc of about 300 000 A/cm2 was obtained by extrapolating the Jc-B curves to zero field. Multifilamentary (seven-core) MgB2 wire was successfully fabricated using Cu-Ni tubes. For both tapes and wires, the grain connectivity of MgB2 was as good as a high-pressure sintered bulk sample. However, the Jc of the Cu-Ni sheathed wire was lower than the stainless steel sheathed tape due to the lower packing density of MgB2.
- Publication:
-
Applied Physics Letters
- Pub Date:
- October 2001
- DOI:
- 10.1063/1.1407856
- arXiv:
- arXiv:cond-mat/0106002
- Bibcode:
- 2001ApPhL..79.2435K
- Keywords:
-
- 74.72.-h;
- 85.25.Kx;
- 74.60.Jg;
- Cuprate superconductors;
- Condensed Matter - Superconductivity
- E-Print:
- 4 pages, 3 figures