Constriction and contact impedance of ceramic solid electrolytes

The development of solid-state batteries is hindered by the degradation of the solid-solid interface during cycling which can cause void formation and contact loss. Here, we systematically investigate the effect of unrecoverable and real interfacial contact area at the electrode/Li$_6$PS$_5$Cl interface on the impedance spectrum. By varying applied stack pressures and controlling contact geometries, we identify their distinct signatures in the impedance spectrum and quantify their influence on the interfacial resistance and effective ionic conductivity of the solid electrolyte. Experimental results demonstrate that higher pressures and improved contact areas significantly reduce interfacial resistance. The interfacial resistance scales with pressure according to power law with exponent of -0.5, providing insights into the variation of real contact area. Further, distributed contacts lead to lower impedance compared to concentrated contacts due to smaller potential gradients and a more uniform potential distribution. Our simulations predict interfacial resistances of the contact geometries in agreement with experiments. Our work emphasizes the distinct roles of unrecoverable and recoverable contact losses in controlling the impedance of solid-state batteries.