On modeling fracture of soft polymers

Soft polymers are ubiquitous materials found in nature and as engineering materials with properties varying from rate-independent to significantly rate-dependent depending on the crosslinking mechanisms. Current fracture toughness measures such as energy release rate are non-unique for rate-dependent soft materials for varying loading profiles and specimen geometries. Works on modeling fracture in rate-dependent soft polymers are limited to crack tip stress field analyses or crack tip driving force approaches for specific pre-cracked geometries. We have developed a model to predict damage initiation and growth in soft polymers based on a generalized multi-mechanism gradient damage framework. We propose and show that a critical value of stress work $\mathit{W}_{cr}$ can uniquely quantify the total energy dissipation per unit referential volume associated with the complete failure of a material point under a loading mode. $\mathit{W}_{cr}$ can be evaluated using homogeneous deformation experiments and without a constitutive model. $\mathit{W}_{cr}$ is demonstrated to be approximately constant with strain rate for two rate-dependent soft polymers and different loading modes for an elastomer. We propose the energetic contribution to $\mathit{W}_{cr}$ as a suitable damage initiation criterion. The proposed initiation criterion in the damage model enabled successful predictions of fracture in an important rate-stiffening soft polymer Polyborosiloxane in a variety of experiments involving different specimen geometries and loading conditions. The model also provides a consistent energy density estimate for fracture-associated microstructural processes in Polyborosiloxane. The broader applicability of the fracture model is shown by its ability to predict fracture in an elastomer (EPDM) and another viscous soft polymer (EPS25 vitrimer).