Electronic properties of the bilayer nickelates R3N i2O7 with oxygen vacancies (R =La or Ce)

The discovery of superconductivity in L a₃N i₂O₇ has sparked significant research interest in the field of nickelate superconductors. Despite extensive studies on pristine L a₃N i₂O₇ , the role of oxygen vacancies (V_O), a common type of intrinsic defect in oxides, on electronic structures and superconductivity in L a₃N i₂O₇ remains unclear. In this paper, we identify that the loss of intrabilayer apical oxygen is the most energetically favorable. The electronic structure undergoes notable changes, particularly for the Ni-d_{z 2} and Ni-d_{x 2 −y 2} orbitals. The d_{z 2} orbital shifts downward, substantially reducing its proportion at the Fermi level. Conversely, the proportion of the d_{x 2 −y 2} state increases due to the orbital localization. Applying the two-band model, the hopping strength between intrabilayer d_{z 2} functions is observed to increase significantly but with opposite signs, which deviates from the previous understanding. The interorbital hopping between d_{z 2} and d_{x 2 −y 2} functions decreases in the presence of V_O. Our results indicate that the formation of V_O could be harmful to the superconductivity in L a₃N i₂O₇ , considering the general assumption regarding the critical role of d_{z 2} in superconductivity generation. Additionally, we propose that C e₃N i₂O₇ , possessing similar electronic structures to L a₃N i₂O₇ , could be a promising nickelate superconductor with a potential low concentration of V_O.